Cored solder wire MARMOT MARMOT ANTICORO

Standard (SnPb) soldering » Standard (SnPb) solders MARMOT » Cored solder wire MARMOT MARMOT ANTICORO

Technical Data Sheet

Pb60Sn39,5Sb0,5 MTV009B

Product name: 

MARMOT Anticoro solder

Description and key properties:

  • Special solder MARMOT Anticoro for soldering stainless steel with flux MTV0009B
  • High efficiency with color metals and steels, allows soldering these materials together
  • For hand and automated soft soldering in engineering
  • For soft soldering by naked flame with high working temperature range 180°C to 750°C
  • Complete replacement for expensive hard Silver soldering
  • The flux does not contain any organic components therefore does not carbonize during soldering
  • Useable everywhere  when water cleaning is applicable

Operating manual:

Soldered place is heat up by the naked flame or by soldering iron and then gradually add required amount of the solder. Residues after soldering must be washed by water. Long term or warm water washing can cause oxidation of the solder surface due to oxygen presented in water.

Used water after cleaning must not be let out without processing to the surface/ground water.

 

  Technical specification

Pb60Sn39,5Sb0,5

Commercial Name:       

MARMOT® Anticoro solder

 

Supplied and shaped as wire with flux MTV009B.

Diameter and Package:

4

mm

Reel

6/10

Kg

 

 List of components:

Alloyed

 

 

Content range

 

 

 

 

U

min.

max.

U

 

Ag 

Silver

 

%

0,000

0,050

%

 

Bi

Bismuth

 

%

0,000

0,050

%

 

Fe

Iron

 

%

0,000

0,020

%

 

P

Phosphorus

 

%

0,000

0,200

%

 

Sb

Antimony

 

%

0,000

0,050

%

 

Al

Aluminium

0,45

%

0,350

0,600

%

 

Cd

Cadmium

 

%

0,000

0,002

%

 

In

Indium

 

%

0,000

0,050

%

 

Pb

Lead

 60,00

%

rest

rest

%

 

As

Arsenic

 

%

0,000

0,010

%

 

Cu

Copper

 

%

0,600

0,050

%

 

Ni

Nickel

 

%

0,030

0,010

%

 

Zn

Zinc

 

%

0,000

0,001

%

 

Sn

Tin

39,55

%

38,50

40,500

%

 

 

 

 

 

 

 

 

 

 Flux:

MTV009B

 3,2

 3

 3,5

%

 

 

 

 

 

 

 

 

 

 

Melting point:

180

°C

 

 

 

 

 

Working temperature*:

240–750

°C

 

 

 

 

 

Working temperature is the temperature when fluidity is the best for soldering